KLEIBERIT 538.1

כמויות יישום ולחץ:

KLEIBERIT 538.1

Properties of the bond Demonstrated with the example of tensile strength according to DIN EN 1465 Material Temperature (°C) Tensile shear strength (N/mm²) aluminium to alumium (ground and degreased) -20 +20 +80 12.5 12.0 11.5 aluminium to steel (ground and degreased) • כמות יישום (תלוי במבנה המשטח ובהתקני היישום): גרם/מ"ר 100-130 : - עבור עבודות פורניר גרם/מ"ר 150-200 : - בהדבקת עץ מלא • . 2 ניוטון/מ"מ 0.70-1.00 :) לחץ לחיצה נדרש (עבור למינציות ועץ למינציה 2C-PUR- Adhesive Properties of the bond Demonstrated with the example of tensile strength according to DIN EN 1465 Material Temperature (°C) Tensile shear

2C-PUR- Adhesive

Fields of application  As adhesive for very high stressed bondings of metals, glass, wood and many plastics to each other  As fixing compound for threads and screws  As moulding for device construction and the like Advantages  Universally applicable, hardens without shrinkage  High resistance to heat and cold  Good ageing properties Properties of the bonding agent Two-component system, free from solvents Base: polyurethane Component A: KLEIBERIT 538.1 Component B: KLEIBERIT 870.0 Specific gravity: טמפרטורה

-20 +20 +80

15.0 14.0 14.2 28.5 27.6 17.6

Fields of application  As adhesive for very high stressed bondings of metals, glass, wood and many plastics to each other  As fixing compound for threads and screws  As moulding for device construction and the like Advantages  Universally applicable, hardens without shrinkage  High resistance to heat and cold  Good ageing properties Properties of the bonding agent Two-component system, free from solvents Base: polyurethane Component A: KLEIBERIT 538.1 Component B: KLEIBERIT 870.0 Specific gravity: Mixing ratio: Viscosity at 20 °C (Brookfield Sp. 4/20rpm): זמן לחיצה מינימלי דקות. 15- מ דקות. 5- מ דקות. 2- מ דקות. 20 דקות עד 15- מ

זמני לחיצה מינימליים (משתנים לפי טמפרטורה)

strength (N/mm²) -20 +20 +80

Steel to steel (ground and degreased)

aluminium to alumium (ground and degreased) aluminium to steel (ground and degreased) Steel to steel (ground and degreased) 200C

-20 +20 +80 -20 +20 +80 -20 +20 +80

12.5 12.0 11.5 15.0 14.0 14.2 28.5 27.6 17.6

יישום

The aluminium broke in test 1 and 2

Properties of the binding material Hardness: 80-85 Shore D (ISO 868) Tensile strength: 45 MPa (ISO 527) Elongation at break: 5.9 % (ISO 527) Modulus of elasticity: 1550 MPa (ISO 527) Bending strengths: 62 MPa (ISO 178) Deflection: 6,5 mm (ISO 178) Linear coefficient of thermal expansion: 6,5•10 -5 .K -1 (-20°C bis +40°C) Water absorbtion: 0,08%

: )Joint bonding( הדבקת מפרקים

Comp. A: approx. 1.52 g/cm³ Comp. B: approx. 1.22 g/cm³ Mixture: approx. 1,41 g/cm³

500C

: (מחומם מראש) הדבקת מפרקים

comp. A:comp. B = 2.5:1 by weight comp. A:comp. B = 2.0:1 by volume

The aluminium broke in test 1 and 2

Colour of the mixture: light-grey

800C

(24 hours at 23°C) הדבקת מפרקים

Properties of the binding material Hardness: 80-85 Shore D (ISO 868) Tensile strength: 45 MPa (ISO 527) Elongation at break: 5.9 % (ISO 527) Modulus of elasticity: 1550 MPa (ISO 527) Bending strengths: 62 MPa (ISO 178) Deflection: 6,5 mm (ISO 178) Linear coefficient of thermal expansion: 6,5•10 -5 .K -1 (-20°C bis +40°C) Water absorbtion: 0,08% 80°C Identification: Comp. B: identification required according to EU regulations, contains 4.4 diphenyl methane diisocyanate (see our safety data sheet). Note : Intended for commercial use only. Application methods  Manual with spatula, brush  Automatically with two component mixing and dosing plant Preparation The surfaces to be glued must be free of rust, dust and grease. Metal and plastic surfaces must be roughened. Remove rust and oxide spots from the metal. 200C 500C 800C (24 hours at 23°C) approx. 30 minutes

:HPL הדבקת משטחי

Comp. A: approx. 1.52 g/cm³ Comp. B: approx. 1.22 g/cm³ Mixture: approx. 1,41 g/cm³ דקות. 5- מ

:HPL הדבקת משטחי

comp. A: 3,200  800 mPa.s comp. B: 150  50 mPa.s mixture: 900  300 mPa.s

comp. A:comp. B = 2.5:1 by weight comp. A:comp. B = 2.0:1 by volume Consistency:

good flowing properties

Mixing ratio:

דקות. 2 דקה עד 1- מ

הדבקת משטחים:

Pot life (100 g mixture at 20°C):

approx. 90 minutes

Colour of the mixture: light-grey

Fixing time (steel sheet, 1 mm thickness, surface 2 cm²)

20°C

50°C

approx. 8 hours

approx. 80 minutes

Comp. B: identification required according to EU regulations, contains 4.4 diphenyl methane diisocyanate (see our safety data sheet). Optimal adhesion of the adhesive to the metal surface is achieved with sanding or sandblasting. Acetone is recommended for cleaning working tools. The ideal working temperature is 20 °C.

Identification: These are guide values only and are dependent on the object.

* ייתכן שיידרש זמן המתנה נוסף של שעתיים לפני עיבוד נוסף, בהתאם לסוג העץ ולתכונות המשטח.

Viscosity at 20 °C (Brookfield Sp. 4/20rpm):

Restricted to professional users

Page 1 of 2

comp. A: 3,200  800 mPa.s comp. B: 150  50 mPa.s mixture: 900  300 mPa.s

Note :

Intended for commercial use only.

Application methods  Manual with spatula, brush  Automatically with two component mixing and dosing plant Preparation The surfaces to be glued must be free of rust, dust and grease. Metal and plastic surfaces must be roughened. Remove rust and oxide spots from the metal. Optimal adhesion of the adhesive to the metal surface is achieved with sanding or sandblasting. Acetone is recommended for cleaning working tools. The ideal working temperature is 20 °C.

Consistency:

good flowing properties

Pot life (100 g mixture at 20°C):

approx. 90 minutes

Fixing time (steel sheet, 1 mm thickness, surface 2 cm²)

20°C

50°C

80°C

approx. 8 hours

approx. 80 minutes

approx. 30 minutes

These are guide values only and are dependent on the object.